6064A aluminium bars
This alloy has good machinability and high mechanical properties. Moreover it has a good resistance to corrosion and suitability to hard, protective and decorative anodizing.
EU YellowUSA #ff9409
According to EU directives: 2000/53/CE (ELV) - 2002/95/CE (RoHS)
Main applications
particulars for braking systems for automotive, structural components for civil constructions, railroad and street heavy vehicles.
Properties
| Property | T6 | T8/T9 |
|---|---|---|
| Machinability | ||
| Protective anodizing | ||
| Decorative anodizing | ||
| Hard anodizing | ||
| Resistance to atmospheric corrosion | ||
| Resistance to marine corrosion | ||
| MIG-TIG weldability | ||
| At resistance weldability | ||
| Brazing weldability | ||
| Plastic formability when cold | ||
| Plastic formability when hot |
Chemical composition
| Element | Range (%) |
|---|---|
| Si | 0,40 ÷ 0,80 |
| Fe | ≤ 0,70 |
| Cu | 0,15 ÷ 0,40 |
| Mn | ≤ 0,15 |
| Mg | 0,80 ÷ 1,20 |
| Cr | 0,04 ÷ 0,14 |
| Ni | — |
| Zn | ≤0,25 |
| Ti | ≤ 0,15 |
| Zr | — |
| Pb | 0,20 ÷ 0,40 |
| Bi | 0,40 ÷ 0,80 |
| Al | Rem. |
Physical characteristics
| Quantity | Unit | Value |
|---|---|---|
| Density | Kg/dm^3 | 2,72 |
| Modulus of elasticity | MPa | 69.000 |
| Coefficient of thermal expansion | x10^-6/C | 23,4 |
| Thermal conductivity at 20°C | W/mk | 172 |
| Electrical resistivity at 20°C | Ωmm^3/m | 0,039 |
Mechanical properties
| — | Temper | Rm MPa | Rp 0,2 MPa | A% | HBW |
|---|---|---|---|---|---|
| Extruded | T6 | 260 | 240 | 10 | 90 |
| Extruded | T6* | 350 | 320 | 10 | 110 |
| Drawn | T6 | 290 | 240 | 10 | 90 |
| Drawn | T6* | 350 | 295 | 12 | 95 |
| Drawn | T8 | 345 | 315 | 4 | 95 |
| Drawn | T8* | 375 | 355 | 10 | 105 |
| Drawn | T9 | 360 | 330 | 4 | 95 |
| Drawn | T9* | 385 | 370 | 7 | 110 |
* Typical Eural Characteristics
Production programme
DRAWN: AA 6064 T6
- Round: 60mm - 250mm
EXTRUDED: AA 6064 T9 *
- Round: 9mm - 80 mm
- Hexagonal: 12mm - 55mm
* also possible in T8