2017A aluminium bars
This alloy has high mechanical properties and excellent resistance to fatigue. During machining, it creates quite long chips, Therefore, it is not well suited for automatic lathes. It can be replaced by 2030 which has the same mechanical properties but has better machinability, allowing higher productivity.
EU Green
According to EU directives: 2000/53/CE (ELV) - 2002/95/CE (RoHS)
Main applications
high structural resistance components for aviation, defence, high resistance components, screws and bolts.
Properties
| Property | T3/T4 |
|---|---|
| Machinability | |
| Protective anodizing | |
| Decorative anodizing | |
| Hard anodizing | |
| Resistance to atmospheric corrosion | |
| Resistance to marine corrosion | |
| MIG-TIG weldability | |
| At resistance weldability | |
| Brazing weldability | |
| Plastic formability when cold | |
| Plastic formability when hot |
Chemical composition
| Element | Range (%) |
|---|---|
| Si | 0,20 ÷ 0,80 |
| Fe | ≤0,70 |
| Cu | 3,5 ÷ 4,5 |
| Mn | 0,40 ÷ 1,00 |
| Mg | 0,40 ÷ 1,00 |
| Cr | ≤ 0,10 |
| Ni | — |
| Zn | ≤0,25 |
| Ti | — |
| Zr | — |
| Pb | — |
| Bi | — |
| Al | Rem. |
Physical characteristics
| Quantity | Unit | Value |
|---|---|---|
| Density | Kg/dm^3 | 2,79 |
| Modulus of elasticity | MPa | 75.000 |
| Coefficient of thermal expansion | x10^-6/C | 23,6 |
| Thermal conductivity at 20°C | W/mk | 134 |
| Electrical resistivity at 20°C | Ωmm^3/m | 0,051 |
Mechanical properties
| — | Temper | Rm MPa | Rp 0,2 MPa | A% | HBW |
|---|---|---|---|---|---|
| Extruded | T4 | 390 | 260 | 9 | 105 |
| Extruded | T4* | 410 | 260 | 11 | 115 |
| Drawn | T3 | 400 | 250 | 10 | 105 |
| Drawn | T3* | 470 | 390 | 11 | 135 |
* Typical Eural Characteristics
Production programme
DRAWN: EN AW 2017A-T3
- Round: 10mm - 80mm
- Square: 20x20mm - 60x60mm
- Flat: 20x15mm - 70x55mm
EXTRUDED: EN AW 2017A T4
- Round: 30mm - 250 mm.
- Square: 50x50mm - 160x160mm
- Flat: 80x40mm - 160x150mm