2007 aluminium bars
Among aluminium alloys for high speed automatic lathes, 2007 and 2030 have the highest mechanical characteristics. This alloy is the most often selected when it is required to have a good combination of machinability and high mechanical properties. It has low corrosion resistance; therefore it is recommended to have a protective anodizing of finished products.
EU Black
Main applications
screws, bolts, nuts, threaded bars
Properties
| Property | T3/T4 |
|---|---|
| Machinability | |
| Protective anodizing | |
| Decorative anodizing | |
| Hard anodizing | |
| Resistance to atmospheric corrosion | |
| Resistance to marine corrosion | |
| MIG-TIG weldability | |
| At resistance weldability | |
| Brazing weldability | |
| Plastic formability when cold | |
| Plastic formability when hot |
Chemical composition
| Element | Range (%) |
|---|---|
| Si | ≤0,80 |
| Fe | ≤0,80 |
| Cu | 3,30 ÷ 4,60 |
| Mn | 0,50 ÷ 1,00 |
| Mg | 0,40 ÷ 1,80 |
| Cr | ≤ 0,10 |
| Ni | ≤ 0,20 |
| Zn | ≤0,80 |
| Ti | ≤ 0,20 |
| Zr | — |
| Pb | 0,80 ÷ 1,00 |
| Bi | ≤ 0,20 |
| Sn | ≤ 0,20 |
| Al | Rem. |
Physical characteristics
| Quantity | Unit | Value |
|---|---|---|
| Density | Kg/dm^3 | 2,85 |
| Modulus of elasticity | MPa | 71.000 |
| Coefficient of thermal expansion | x10^-6/C | 23,5 |
| Thermal conductivity at 20°C | W/mk | 140 |
| Electrical resistivity at 20°C | Ωmm^3/m | 0,057 |
Mechanical properties
| — | Temper | Rm MPa | Rp 0,2 MPa | A% | HBW |
|---|---|---|---|---|---|
| Extruded | T4 | 370 | 250 | 8 | 95 |
| Extruded | T4* | 440 | 300 | 12 | 125 |
| Drawn | T3 | 370 | 240 | 7 | 95 |
| Drawn | T3* | 465 | 410 | 8 | 125 |
* Typical Eural Characteristics