This alloy has been developed by EURAL and it is one of the best for high speed automatic lathes. It gives the following advantages:

Easy machining with any tool
Excellent chip forming performance (thin chip)
Longer tool life
High mechanical properties
Better anodizing and weldability attitude compared to alloys 2011, 2007, 2030.

This alloy does not contain neither lead nor tin and therefore it is a good solution for the production of parts under the latest restriction on this topic (2018/740/EU RoHS: Pb ≤ 0,1 starting from 18/05/2021).

Main applications

automotive industry, electric and electronic industry, precision machining, defense, forging, screws, bolts, nuts, threaded parts of thin thickness.

Properties

Properties	T3/T6	T8
Machinability
Protective anodizing
Decorative anodizing
Hard anodizing
Resistance to atmospheric corrosion
Resistance to marine corrosion
MIG-TIG weldability
At resistance weldability
Brazing weldability
Plastic formability when cold
Plastic formability when hot

Excellent

Good

Acceptable

Not recommended

Chemical composition

Si	0,10 ÷ 1,20
Fe	≤0,70
Cu	2,20 ÷ 2,70
Mn	0,40 ÷ 1,00
Mg	0,20 ÷ 0,60
Cr	≤ 0,15
Ni	≤ 0,15
Zn	≤0,50
Ti	≤ 0,10
Bi	0,05 ÷ 0,80

Others	Each 0,05 Total 0,15
Al	Remainderer

Physical characteristics

Density	Kg/dm^3	2,77
Modulus of elasticity	MPa	70.000
Coefficient of thermal expansion	x10^-6/C	22,9
Thermal conductivity at 20°C	W/mk	T3: 151 T8: 173
Electrical resistivity at 20°C	Ωmm^3/m	T3: 0,046 T8: 0,046

Mechanical properties

	Temper	Diam. mm	Rm MPa	Rp 0,2 MPa	A%	HBW
Drawn	T3	≤ 30	370	240	7	100
	T3	30 <D≤80	340	220	7	100
	T351	≤80	370	240	5	100
	T8	≤80	370	270	8	100
Extruded	T6	≤80	370	250	8	100
Extruded	T6	80 <D≤250	340	220	8	100

Production Programme

DRAWN

Round: 5 ÷ 76,2
Square: 10 ÷ 65
Rectangle: Thick. 12 ÷ 55
Hexagonal: 10 ÷ 63,5

EXTRUDED

Round: 30 ÷ 254
Square: 30 ÷ 165
Rectangle: Thick. 30 ÷ 127
Hexagonal: -