6026LF
According to EU directives: 2000/53/EU (ELV) – 2011/65/EU (RoHS II)
Presentation
This innovative alloy has been conceived and developed in Eural Gnutti SpA’s research laboratories, in order to meet the most recent standards for the protection of the environment, removing lead. It is particularly suitable for being machined on high speed automatic lathes. It has good resistance to corrosion, medium-high mechanical properties, good suitability for decorative and industrial hard anodizing. It is also used for hot forging purposes.
Eural 6026LF alloy does not contain tin (Sn) which, as it has been proved, causes weakness and cracking of the machined parts when submitted to stress and high temperature.
Due to its brittle nature, tin has the dangerous tendency to suddenly break without signifi cant previous deformation (strain).
It can replace 2007, 2011, 2015, 2028, 2030, 2044, 6012, 6012A, 6020, 6021, 6023, 6028, 6033, 6040, 6041, 6042, 6061, 6065, 6082, 6262, 6064A, 6262A, 6351, 7020 alloys.
Main applications
automotive industry, electric and electronic industry, hot forging, screws, bolts, nuts, threaded parts.
Properties
Properties | T6 | T8/T9 |
---|---|---|
Machinability | ||
Protective anodizing | ||
Decorative anodizing | ||
Hard anodizing | ||
Resistance to atmospheric corrosion | ||
Resistance to marine corrosion | ||
MIG-TIG weldability | ||
At resistance weldability | ||
Brazing weldability | ||
Plastic formability when cold | ||
Plastic formability when hot |
Excellent
Good
Acceptable
Not recommended
Chemical composition
Si | 0,60 ÷ 1,40 |
Fe | ≤0,70 |
Cu | 0,20 ÷ 0,50 |
Mn | 0,20 ÷ 1,00 |
Mg | 0,20 ÷ 1,20 |
Cr | ≤0,30 |
Ni | |
Zn | ≤0,30 |
Ti | ≤0,20 |
Sn | ≤0,05 |
Pb | ≤0,05* (traces) |
Bi | 0,50 ÷ 1,50 |
Others | Each 0,05 Total 0,15 |
Al | Rem |
*6026 is registered with Pb ≤ 0,40
Physical characteristics
Density | Kg/dm^3 |
2,72 |
Modulus of elasticity | MPa |
69.000 |
Coefficient of thermal expansion |
x10^-6/C
|
23,4 |
Thermal conductivity at 20°C |
W/mk
|
172 |
Electrical resistivity at 20°C |
Ωmm^3/m
|
0,039 |
Mechanical properties
Temper | Diam. mm | Rm MPa |
Rp 0,2 MPa |
A% | HBW | |
---|---|---|---|---|---|---|
Drawn | T6 | ≤80 | 370 | 300 | 8 | 95 |
T8 | ≤80 | 345 | 315 | 4 | 95 | |
T9 | ≤80 | 360 | 330 | 4 | 95 | |
Extruded | T6 | ≤ 140 | 370 | 300 | 8 | 95 |
T6 | 140 < D ≤ 200 | 340 | 250 | 8 | 90 | |
T6 | 200 < D ≤ 250 | 300 | 200 | 8 | 90 |
Production Programme
DRAWN: T8, T8, T9
- Round: 6 - 76,2
- Square: 10 - 65
- Flat: Spess. 12 - 55
- Hexagonal: 10 - 63,5
EXTRUDED: T6
- Round: 30 - 254
- Square: 50 - 165
- Flat: Spess. 30 - 157